Argorev Impreso

Argorev Impreso mortar is idea for theme work for facing exterior and interior walls and as a regulating layer. This product has been designed to be impermeable to rainwater, and once mixed it can be applied by hand or mechanically at different thicknesses, to achieve a final look by stamping with moulds or modelling by hand.

The approximate yield of ARGOREV IMPRESO is 2.0 kg/mm/m².

25 kg sacks (1000 kg pallet).

In the original container in a covered area, for up to 12 months.

The support should be sturdy, flat, as rough as possible and free of dust, paint, oil, formwork remover, etc.
At joints between different materials, angles or special areas with a risk of cracking, reinforce the mortar with fibreglass mesh embedded into the mortar and overlapping the joint by about 20 cm.
On smooth surfaces such as concrete or non-absorbent surfaces, apply a primer coat to improve the adherence before applying the mortar.
At high temperatures and/or in dry winds, it is advisable to wet the support in advance to prevent the mortar from drying out, wetting again 24 hours after application.
 

1. Mix mechanically with clean water until an even, plastic mixture is achieved, without any lumps, using 20% water (approx. 5 l/sack).
2. Leave the mixture to stand for 5 minutes and then remix before applying.
3. For facing, spread with a spraying machine or trowel onto the support, applying a first layer that is quite thin and well compacted, followed by the rest of the material to achieve a minimum thickness of 12–15 mm. Then smooth until level. If thicknesses of over 20 mm are required, use several layers.
4. Apply the desired technique: Moulding, modelling, etc. ARGOREV IMPRESO is suitable for use with coloured acids to create irregular colour effects.

Do not apply onto gypsum-based surfaces.
Do not apply onto supports or parts with poor or zero absorption.
Do not apply at extreme temperatures (below 5 ºC or above 35 ºC).
 

Mixing water approx. (%): 20
Max. aggregate size (mm): 2
Apparent paste density (g/cm³): 1.7
Apparent hard density (g/cm³): 1.5
Lifetime of mix (mins): 120
Bending strength (N/mm²): ≥2.5
Crushing strength (N/mm²): ≥6.0
Tensile strength (N/mm²): ≥0.3
Capillarity (dm².min½): <0.5